Nokorode regular paste flux is a lead free, all purpose, soft soldering paste flux ideal for use with 95/5 and other common solders. Nokorode special oil base protects the solder joint against corrosive attack. It cleans and fluxes all at one time. When heated, it reduces surface tension and allows the solder to flow easily and uniformly into the joint. Nokorode regular paste flux works to deliver a strong, leak free joint. It's non­aggressive formula is ideal when used on copper and brass fittings.

• Will not freeze or decompose
• No odor, lead free

,
,

RectorSeal T720-59

Lead free solder widely used in plumbing applications where lead-bearing solders are prohibited. Contains nickel, making joints tremendously strong. Wide range makes bridgit an excellent alloy for large diameter fittings and ill-fitted or non-concentric pipes. Fills gaps and caps off easily and effectively.

Sid Harvey Item #:T720: Replaces Part #:'s : 15204,
,

Designed primarily for copper to copper and copper to brass connections the paste form is ideal for soldering tube joints. Not recommended for electrical or electronic applications due to the potential corrosive residue of the flux. Stay Clean paste flux works well with most leaded and lead-free solder compositions. Flux residue should be removed after soldering.

Sid Harvey Item #:T720-25A: Replaces Part #:'s : 14954,
,

Harris T720-25A

Stay Brite solders bond with all of the ferrous and nonferrous alloys. Joints soldered with Stay Brite solders exhibit considerably higher than necessary elongation for sound, dissimilar metal joints and vibration applications. Both Stay Brite and Stay Brite 8 produce an overall component with greater strength than a brazed component whose base metals are weakened by annealment from high brazing heat.

• 14000 psi tensile strength
• 10600 psi shear strength
• Bright silver color
• 430 deg F solidus and liquids temperature
• 48% elongation
• 16.4 electrical conductivity
• Lead free Harris Stay Brite SB61 Lead free Solder Wire, 1/8", 450 deg F, 1 lb Spool, Silver/Tin,
  ,
  
  
  
  

  Harris T720-11

Harris Stay-Clean SCLF16 Clear to Slightly Yellow General Purpose Soldering Flux, 16 oz, Plastic Bottle

• A general purpose zinc chloride flux for soldering with all soft solders use with tin-lead solder, tin-antimony solder, Stay-Brite solder Harris Stay-Clean SCLF16 Clear to Slightly Yellow General Purpose Soldering Flux, 16 oz, Plastic BottleSid Harvey Item #:T720-51: Replaces Part #:'s : 10921,
  ,
  
  
  

Harris T720-55 An all-purpose, low-temperature flux for use in silver brazing. Use with most ferrous and non ferrous metals, not recommended on aluminum, magnesium, and titanium.

• Flux may be water thinned but care should be taken to avoid excess dilution
• Flux turns clear, (transparent), close to brazing application temperature
• Burns eyes and skin can be fatal if swallowed
• Fukes and gases can be hazardous to your health
• Heat rays, (infrared radiation) from flame or hot metal can injure eyes

,
,

Harris T720-24E All-Braz Solder Kit,
,

Harris T720-19 Stay-Silv 5 is well suited where close fit-up cannot be maintained. Stay-Silv 5 is somewhat more ductile than Harris 0 or Stay-Silv 2

• 1/8" x .050 x 20" brazing sticks
• Chemical Composition: 5% Silver, 6% Phosphorus, Balance Copper
• Specifications: AWS/A5.8 Class BCuP-3, ASMESFA5.8 Class BCuP-3, QQB-650B Class BCuP-3
• Liquidus Temperature: 1500°F (816°C)
• Solidus Temperature: 1190°F (643°C)

Sid Harvey Item #:T720-19: Replaces Part #:'s : 15199,
,

Harris T720-19

Harris .05" x 1/8" Flat x 20" Stay-Silv 15 Silver Solder is ideal for most copper-to-copper or brass joints where good fit-up exists. This filler metal is excellent for situations in which close fit-up does not exist, and where agitation and vibration in service are involved

• Alloy Material: 15% Silver 5% Phosphor 80% Copper
• Diameter: 1/8"
• Trade Name: Stay-Silv
• AWS Classification: BCuP-5
• Solder Type: Flat Brazing Alloy Filler Metal
• Length: 20 in

Sid Harvey Item #:T720-20: Replaces Part #:'s : T720-20A,
,

Harris 95561 Lead Free Solder, 1/8", 1 lb Spool

• Tin-antimony solder well suited for applications where moderately elevated temperature is a factor
• With higher electrical conductivity and high fluidity, 95/5 is recommended for lead free installation of small diameter, tight fitting connections
• Not recommended for use on brass or HVAC connections
• 95 - 5 tin/antimony solder is a low temperature lead free solder with a narrow melting range
• The rapid melting characteristics require close fitting connections as it is difficult bridge or fill wide clearance

Sid Harvey Item #:T720-6: Replaces Part #:'s : 15202,
,

Harris T720-6

Both Stay Brite and Stay Brite 8 produce an overall component with greater strength than a brazed component whose base metals are weakened by annealment from high brazing heat. Stay Brite solders bond with all of the ferrous and nonferrous alloys. Joints soldered with Stay Brite solders exhibit considerably higher than necessary elongation for sound, dissimilar metal joints and vibration applications.

Sid Harvey Item #:T720-12: Replaces Part #:'s : 15207,
,

Designed primarily for copper to copper and copper to brass connections the paste form is ideal for soldering tube joints. Not recommended for electrical or electronic applications due to the potential corrosive residue of the flux. Stay Clean paste flux works well with most leaded and lead-free solder compositions. Flux residue should be removed after soldering.

,
,